The corrosion inhibition power of an eco-friendly green inhibitor Ixora coccinea extract (ICE) for mild steel in 1 M HCl and 0.5 M H2SO₄ was analysed using physicochemical and electrochemical techniques. 1–5 v/v% ICE was prepared and added into the corrosive acidic media for different analyses. Weight loss measurements conducted for a period of 24hrs for mild steel immersion revealed 89.38% and 77.96% inhibition capacity of ICE in 1 M HCl and 0.5 M H2SO₄ medium respectively. Electrochemical impedance parameters show that as concentration is increased, efficiency increases and double layer capacitance decreases. Potentiodynamic polarization techniques are also in good agreement with impedance studies and exhibit the mixed type inhibition character of ICE. Electrochemical noise spectrum also strongly supports the anti-corrosive property of ICE and the magnitude of noise signal decreases concerning the increase in ICE concentration. Ixorene, which is one of the major constituents of Ixora coccinea leaves was also studied for its corrosion inhibition nature by quantum mechanical calculations and was found to match with all other results. Adsorption studies of ICE are in accordance with Langmuir isotherm. Surface morphological studies confirm the formation of a protective barrier on mild steel surface in both media, i.e., 1 M HCl and 0.5 M H2SO₄.

The corrosion inhibition efficiency of the Schiff base N,N’-(5,5-dimethylcyclohexane-1,3-diylidene)dianiline (DmChDa) on mild steel in 1M HCl and 0.5M H₂SO₄ was evaluated using gravimetric, electrochemical impedance spectroscopy, potentiodynamic polarization and electrochemical noise measurement. Experimental results established that DmChDa possess relatively high corrosion inhibition capacity. Langmuir and El-Awady adsorption isotherms were obeyed by the Schiff base in 1M HCl and 0.5M H₂SO₄ respectively. SEM analysis showed that DmChDa was adsorbed on the steel surface during corrosion inhibition. The variation of metal dissolution with temperature was also examined using gravimetric study.

Two heterocyclic Schiff bases namely (E)-2-(1-(2-phenylhydrazono)ethyl)pyridine (or 2-acetyl pyridine phenyl hydrazone) (2APPH) and (E)-2-(1-triazylidineethyl)pyridine (or 2-acetyl pyridine semicarbazone) (2APSC) were synthesized, characterized and their corrosion inhibition behaviour as well as mechanism of inhibition were investigated by different techniques. Structural characterization includes NMR, Mass, IR and UV-visible spectroscopy and elemental analysis. Corrosion inhibition behaviour of aforesaid compounds on mild steel in 1M hydrochloric acid was examined by electrochemical methods including potentiodynamic polarization analysis and electrochemical impedance spectroscopic techniques. The mechanism of corrosion inhibition was explored and supplemented by adsorption and surface morphological studies. Quantum mechanical investigations on corrosion behaviour of compounds were also conducted and satisfying correlation was noticed between the results of corrosion measurement methods and quantum mechanical evaluations.